SikaEmaco® N 202

One Component, Economical, Polymer Modified, Pore Sealer / Finishing Mortar

No image available

SikaEmaco® N 202 is a cementitious, silica fume containing, polymer modified one component pore sealer and finishing mortar.
Suitable for use in hot and tropical climatic conditions.

  • Easy to use
  • Excellent workability
  • Good mechanical strengths
  • Can be applied by wet-spray method
  • Non-corrosive
  • Adjustable "creamy" consistency
  • Economical
Product Data Sheet Show all documents

Overview

Usage

SikaEmaco® N 202 can be used as a:
  • Pore sealer / finishing mortar on cementitious substrates
  • Thin layer rendering and smoothing on horizontal and vertical areas in building and civil engineering construction, for external and internal finishing, etc.
  • Levelling mortar on uneven substrates, and profiled concrete surfaces.
  • Repair mortar to fill honeycombs, pores etc.
  • Repair mortar for repair of small defects on edges and joint sides; to form and finish joints and covings.
 

Advantages

  • Easy to use
  • Excellent workability
  • Good mechanical strengths
  • Can be applied by wet-spray method
  • Non-corrosive
  • Adjustable "creamy" consistency
  • Economical

Packaging

25 kg bag

Colour

Grey Powder

Product Details

Composition

Polymer containing cementitious mortar with different additives

Shelf life

12 months from production date.

Storage conditions

Store in undamaged, unopened, original sealed packaging in dry conditions at temperatures between 5 °C and 35 °C. Protect from direct sunlight, heat and moisture.

Maximum grain size

~ 0.1 mm

Compressive strength

7 days

28 days

w/p ratio = 0.30~ 20 N/mm2~ 30 N/mm2

Application

Fresh mortar density

~ 1.90 kg/l

Layer thickness

~ 0.3mm - 3.0mm in one single layer

Ambient air temperature

+5 °C min. / +40 °C max.

Mixing ratio

7.5 litres of water per 25 kg bag

Substrate temperature

+5 °C min. / +40 °C max.

Pot Life

~35 min (25 °C)

Yield

~ 17.0 litres per 25 kg bag

MIXING

SikaEmaco® N 202 can be mixed with a low speed (< 500 rpm) hand drill mixer or using a force action mixer. Pour the recommended water in a suitable, clean mixing container. While stirring slowly, add the powder to the water and mix thoroughly at least for 3 minutes to acheive required homogeneous consistency. The obtained mix should be very creamy, easily spreadable and thixotropic.
Do not add extra water or other ingredients after mixing.
Normal tumble type concrete mixers are not suitable.
Do not mix more material than can be placed within its pot life.

APPLICATION

SikaEmaco® N 202 can be applied by trowel, spatula or wet spray. As soon as the mortar has started to set it can be smoothed by wooden or synthetic float, XPS block or sponge. No additional water should be used, as it may lead to surface discoloration.

CURING TREATMENT

Where ambient conditions may lead to rapid surface drying, the use of light water fogging for 48 hours or application of a suitable water based curing compound like Antisol®-WB is recommended. Do not commence fogging until final set has been reached.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be mechanically removed.

 